文档编号:CL021 文档字数:7477,页数:16 摘要：以枇杷核为原料，研究枇杷核淀粉薄膜的制备工艺。探讨了在淀粉、海藻酸钠、甘油和卡拉胶对枇杷核淀粉薄膜机械性能等的单因素试验的基础上，通过中心组合试验设计获得最佳制备工艺。结果表明，甘油和淀粉对膜的断裂伸长率、拉伸强度和透油性均有显著影响，卡拉胶对膜的断裂伸长率有显著影响，海藻酸钠对膜的透油性有显著影响。最佳生产条件：淀粉68g·L-1，海藻酸钠7g·L-1，甘油11.25mL·L-1，卡拉胶1.25 g·L-1。本实验的制备工艺，能很好保证可食性枇杷核淀粉薄膜具有良好的机械性能，适合进一步中试放大，对可食性淀粉膜的制备材料选择、工艺条件及膜的应用进行了研究 。结果表明：以枇杷核淀粉为成膜主体，配甘油(增塑剂)和海藻酸纳和卡拉胶，即可得到比较理想的可食性淀粉膜。 Abstract: Research preparation process of edible films of Loquat core starch, Yuhang County, Zhejiang Province Tangxi loquat cores as raw materials; On the single-factor test of starch, sodium alginate, glycerol and carrageenan, through the central composite experimental design and the response surface Methodology (RSM) analysis and optimization for preparation process. Glycerol and starch have a significant impact on the elongation at break, tensile strength and oil permeability of the film, carrageenan has a significant influence on elongation at break of the film , sodium alginate have a significant impact on oil permeability of the film. The optimum preparation process was determined as: starch 68 g·L-1, sodium alginate 7 g·L-1, glycerol 11.25 mL·L-1 and carrageenan 1.25 g·L-1.In this study, the preparation process can ensure the good mechanical properties of edible films of loquat core starch，and easy to scale-up. Edible starch in this experiment, membrane material selection, process conditions and the application of film studies. The results showed that: The loquat core starch as the main film, with glycerol (plasticizer) and sodium alginate and carrageenan, could be ideal edible starch film. 目 录
|
|
| |
| 上一篇：聚羧酸盐混凝土减水剂的合成 | 下一篇：混凝土高效减水剂的合成 |
| 推荐论文 | 本专业最新论文 |
| Tags：枇杷 加工 淀粉 研究 | 2011-04-03 08:54:48【返回顶部】 |