分散染料印花用合成增稠剂的合成

文档编号:CL024  文档字数:9860,页数:22

摘  要：相对于天然改性类糊料，我国在合成增稠剂方面的研究工作相对较少，文献报道不多，性能和国外产品有较大差距。本文研究聚丙烯酸盐增稠剂的合成条件包括各种组分的用量、反应温度、通氮排氧、保温时间等因素对增稠剂性能的影响，得出控制最高反应温度在75℃并且尽量延长在较低温度下的反应时间；单独采用KPS为引发剂，用量选择在单体质量的4‰；转相剂的用量与乳化剂用量的比例接近于1：1；丙烯酸用量和丙烯酰胺用量比例在3.7：1最佳，为综合性能较好的分散染料印花用增稠剂。

关键词：增稠剂；聚丙烯酸盐；反相乳液聚合；分散染料印花用增稠剂

Abstract: Compared with the type of paste modified natural, fewer researches are did in synthetic thickener in China, and little reported in the literature. There is a wide gap in the performance of thickener between foreign products and domestic products. In this paper, the synthesis conditions of polyacrylate thickeners include the various components of the dosage, reaction temperature, nitrogen ranked pass oxygen, holding time and other factors affected the performance of the thickener. Control the maximum reaction temperature at 75 ℃ and extend the reaction time at a relatively low temperature as long as possible. Use KPS as initiator, the amount in the quality of the monomer is 4 %; the proportion of transfer agent’s amount and emulsifier’s is close to 1:1; the usage of Acrylic Acid and Acrylamide in the ratio of 3.7:1 can reach the best overall performance for the better use of disperse dyes printing thickener.

Keywords：Thickener; Polyacrylate; Inverse emulsion; Disperse Printing Thickener

目  录
中文摘要 I
英文摘要 II
目录 III
1. 绪论 1
 1.1 反相乳液聚合法概述 1
 1.2 反相乳液聚合的稳定性 2
 1.3 影响产品增稠性能的因素 3
 1.3.1 单体 4
 1.3.2 中和度 4
 1.3.3 引发剂 4
 1.3.4 交联剂 4
 1.3.5 反应温度 4
 1.4 染料印花用糊料的性能 4
 1.4.1 物理性能 5
 1.4.2 化学性能 5
 1.5 印花原糊的流变性和触变性 5
 1.6 国内外印花合成增稠剂的发展现状 5
2. 实验部分 8
 2.1 主要原料与试剂 8
 2.2 主要实验仪器 8
 2.3 实验配方 9
 2.4 实验流程及工艺 9
 2.4.1 实验流程 9
 2.4.2 实验工艺 10
3. 结果与讨论 13
 3.1 影响因素讨论 13
 3.1.1 温度的影响 13
 3.2.1 引发剂用量的影响 13
 3.3.1 转相剂用量的影响 14
 3.4.1 丙烯酸用量和丙烯酰胺用量比例的影响 15
 3.5.1 乳化剂用量的影响 15
 3.2 结论 15
4．总结与展望 16
致谢 17
参考文献 18

相关论文