亚硫酸化蓖麻油的制备及其皮革加脂性能研究

文档编号:HG202  文档字数:11946,页数:28

摘要 ：本文档研究了用马来酸酐对蓖麻油的部分酯化，再用亚硫酸钠进行亚硫酸化，使不溶于水的蓖麻油改性成为能溶于水的蓖麻油改性产品。文档重点考察了酯化温度,蓖麻油与马来酸酐的物质量比,马来酸酐与亚硫酸钠的物质量比对酯化和亚硫酸化的影响，通过测定混合物中马来酸酐的含量、羟值和碘值，得出在110℃条件下,马来酸酐与蓖麻油的物质量之比为1.1:1，马来酸酐与亚硫酸钠的物质量比为1.67:1时，所得的产品性能最好。自制产品与国内外先进加脂剂进行性能比较,讨论了自制产品的加脂性能。
关键词 ：马来酸酐；蓖麻油；亚硫酸钠；改性
中文摘要
 
Abstract ：In this paper, modified products of castor oil which can dissolve in water was prepared through castor oil partially esterified by maleic anhydride, sulfited by sodium sulfite. The thesis has been investigated especially in esterification temperature, the mole ratio of castor oil and malaysian and its effect on esterification and sulfiting. The result of mixture’s content of the malaysian acid anhydride、hydroxyl value、iodine value confirmed that the production which attained at 110℃, the mole ratio of malaysian acid anhydride and castor oil is 1.1:1, the mole ratio of maleic anhydride and sodium sulfite is 1.67:1 has the  best properties. The thesis also discussed the leather stuffing properties compared with domestic and international.
Keywords：malaysian acid anhydride; castor oil ;sodium sulfite; modified.

英文翻译
 目录
中文摘要 1
英文翻译 II
目录 III
1.前言 1
1.1皮革行业在我国的现状 1
1.2加脂剂的作用 1
1.3加脂剂的种类性能 2
1.4蓖麻油的性能 2
2.实验部分 4
2.1主要试剂、原料、反应器 4
2.2亚硫酸化蓖麻油的制备 5
2.2.1蓖麻油改性的工艺流程 5
2.2.2改性蓖麻油的制备 6
2.3加脂实验 6
2.4产品分析测试 6
2.4.1表面张力的测定 6
2.4.2电导率的测定 7
2.4.3混合物中马来酸酐含量的测定 7
2.4.4羟值的测定  8
2.4.5碘值的测定 8
3.结果与讨论 10
3.1合成反应示意图 10
3.2混合物中马来酸酐的测定及其动力学曲线 10
3.3温度对蓖麻油马来酸酐酯化反应的影响 12
3.4原料比对实验产生的影响 13
3.4.1马来酸酐与蓖麻油的不同配比对实验的影响 13
3.4.2亚硫酸钠与马来酸酐不同配比对亚硫酸化的影响 13
3.5亚硫酸化后产品的稳定性 14
3.6与国内外同类产品性能比较 15
4.结论 16
致 谢 17
参考文献 18

相关论文