合金表面连续激光涂覆技术的研究

机械设计制造及其自动化文档，文档编号:JX1281  文档字数:15662.页数:34

摘要
 综述了目前国内外在连续激光非晶化方面的研究和发展。由于非晶态具有晶态金属难以达到的高强度，高韧性，高磁导率和高耐蚀性等等，用高能激光束直接在金属表面快速加热，依靠金属本体的快速热传导冷却而获得非晶层的研究一直引起广泛的注意。但至今还无法使激光非晶化的优势得以发挥。本文采用40Gr作为基体材料进行表面激光涂覆。我们制备了FeMoYB合金材料，这是一种新发现的具有比较高的非晶形成能力的四元合金，研究发现这种合金材料能在铜模注射下能获得一个直径为6.5mm的圆柱棒。我们把FeMoYB材料磨成粉末作为涂覆粉末，采用预先置入法进行激光涂覆。对基体材料进行金相分析，讨论结果。
关键词:  连续激光  激光涂覆  金相分析

Abstract
 This paper summarizes the research and development of CW laser glazing．As the amorphous metal has a crystalline difficult to achieve high strength, high toughness, high permeability and high corrosion resistance and so on, with high-energy laser beam directly on the metal surface rapid heating, the metal body to rely on the rapid heat conduction cooling and to obtain non - layer has been a source of a wide range of research attention. But so far unable to make the advantages of laser amorphization to play an important role. In this paper, 40Gr as a matrix material coating the surface of the laser.In this work, FeMoYB BMGs have been developed.It is found that a fully amorphous FeMoYB cylindrical rod with 6.5mm in diameter can be prepared by copper mold injection.These alloys have a high glass transition. Fe68Mo4Y6B22 ground into a powder as a coating material powder, pre-implantation laser coating method. Matrix materials for phase analysis, the outcome of the discussion.
Keywords：  Cw laser，Laser coating，Metallographic analysis.
 
 
目  录
中文摘要 i
英文摘要 ii
第一章  绪论 1
1.1 研究的背景 1
1.2 研究的意义 1
第二章 激光涂覆概述 3
2.1 激光表面涂覆 3
2.2 激光表面涂覆工艺的特点 3
2.3 涂覆层的形状 5
第三章  Fe–M–Y–B的研究 6
3.1 前言 6
3.2实验 6
3.3结果和讨论 7
3.4结论 9
第四章 涂覆粉末的制备 10
4.1 试样材料的选择 10
4.2试样的熔炼 10
4.3捣碎 11
4.4球磨 12
4.4.1 球磨设备：行星式球磨机和球磨罐 13
4.4.2 清洗球磨罐 15
4.4.3 球磨 15
4.4.4磨完后清洗球磨罐 16
4.4.5真空烘干箱子 16
第五章 激光涂覆 17
5.1  3kW CO2横流激光器多功能加工系统 17
5.2粘接合金粉 19
5.3激光表面熔覆 20
第六章 金相分析 21
6.1 金相试样 21
6.2金相显微镜 21
6.3金相分析 23
第七章 结论 25
致谢 27

相关论文