钢管表面涂层工艺研究

材料成型及控制工程文档，文档编号:JX1390  文档字数:15293.页数:26

摘  要
 随着人类文明的不断发展，钢铁类制品在生产，生活中的用途越来越广泛。因为钢铁在裸露的环境下容易生锈腐蚀，对钢铁产品进行防护，提高其耐腐蚀性非常需要。
 本文主要是通过实验对镍磷合金的配制，粉末的制作以及将其涂覆在钢管表面进行研究。Ni-P合金粉末的制作是依靠气雾法制得，用聚乙稀醇配成胶体使用点胶技术均匀的涂覆在钢管表面，然后在管式链炉中烧结，通过氨分解保护形成镀层。烧结后的钢管表面光亮耐腐蚀，延长了使用寿命。
关键词：Ni-P合金  气雾法制备  聚乙烯醇  烧结工艺
 
Abstract
 With the continuous development of human civilization, steel products in production and daily life in the increasingly wide use. Because the exposed steel in the environment easily rust corrosion protection for steel products, improve its corrosion resistance is required.   This paper is mainly through experiments on the preparation of nickel-phosphorus alloy, powder production and its surface coated steel pipe in the study. Ni-P alloy powder production is to rely on the rule of law in the aerosol, with the use of colloidal PVA alcohol match even the technical point of plastic pipe in the surface coating, and then in the chain-sintering furnace, protected by a coating of ammonia decomposition. Sintering the bright surface of corrosion-resistant steel pipe to extend the service life.
Keywords： Nickel-Phosphorus Alloy  Aerosol Preparation  PVA Sintering Technology
 
目   录
中文摘要 i
Abstract．ii
目　录．iii
第一章　绪论１
 1.1  引言．．1
 1.2  钢管表面处理的方法．．1
 1.3  国内外钢管表面处理技术1
第二章 钢管表面涂层技术与材料的应用和发展．3
 2.1钢管外表面防腐涂层材料的种类．．3
 2.2现代表面涂层技术．7
第三章 钢管表面涂层材料Ni-P合金研究12
 3.1 镍磷合金镀层的现状12
 3.2 镍磷合金镀层的性能优点．12
 3.3 镍磷合金粉制备．12
 3.3.1镍磷中间合金的制备 12
 3.3.2镍磷合金粉制作设备．13
 3.3.3气雾法技术．．13
 3.3.4气雾法制备镍磷合金粉．14
第四章 涂层材料混合液的研究．．16
 4.1 聚乙烯醇的概念和性质．16
 4.2聚乙烯醇的水溶解方法．16
 4.3聚乙稀醇与Ni-P合金制胶17
第五章 钢管表面Ni-P合金镀的烧结工艺流程．．18
 5.1 烧结的概念18
 5.2 钢管烧结工艺的流程18
第六章 钢管的性能测试．20
第七章 结论21
参考文献 22
致谢 23

相关论文